SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product will be phased out per January 2015 -- Lexan* DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.0500 %
0.0500 %
50% RH, 24 hrs; ASTM D570
0.140 %
0.140 %
23°C / 50% RH; ISO 62
Moisture Absorption at Equilibrium 0.14 %
0.14 %
50% RH; ASTM D570
0.30 %
0.30 %
ASTM D570
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 17.1 g/10 min

@Load 1.20 kg,
Temperature 300 °C
17.1 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 1.20 kg,
Temperature 300 °C
16 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
50 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 77.0 MPa
11200 psi
Type I, 50 mm/min; ASTM D638
77.0 MPa
11200 psi
50 mm/min; ISO 527
Elongation at Break 60 %
60 %
50 mm/min; ISO 527
92 %
92 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
8.0 %
8.0 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.83 GPa
410 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 101 MPa
14600 psi
2 mm/min; ISO 178
116 MPa
16800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.31 GPa
335 ksi
2 mm/min; ISO 178
2.63 GPa
381 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
0.320 J/cm

@Temperature -30.0 °C
0.599 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*3; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
93.0 kJ/m²

@Temperature -30.0 °C
44.3 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
13.3 J/cm²

@Temperature -30.0 °C
63.3 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 68.0 J

@Temperature 23.0 °C
50.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
33.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
60.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
33.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 134 °C
273 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 138 °C
280 °F
Rate B/50; ASTM D1525
141 °C
286 °F
Rate B/50; ISO 306
142 °C
288 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL 94
Optical Properties Metric English Comments
Refractive Index 1.584
1.584
ASTM D542
1.584
1.584
ISO 489
Haze <= 0.80 %

@Thickness 2.54 mm
<= 0.80 %

@Thickness 0.100 in
ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2
Erichson scratch depth, 6N 14micrometer
SABIC Method
Pencil Hardness test, 1kgf F
ASTM D3363
Specific Volume 0.85cm^3/g
ASTM D792