SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* DMX1132 is a high flow polycarbonate copolymer resin with improved ammonia resistance over regular polycarbonate resin.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
1.19 g/cc
0.0430 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 38.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
38.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 36 g/10 min

@Load 1.20 kg,
Temperature 300 °C
36 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 110 MPa
16000 psi
ISO 2039-1
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 69.0 MPa
10000 psi
Type I, 50 mm/min; ASTM D638
73.0 MPa
10600 psi
50 mm/min; ISO 527
Elongation at Break >= 25 %
>= 25 %
50 mm/min; ISO 527
50 %
50 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.55 GPa
370 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
2 mm/min; ISO 178
110 MPa
16000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.51 GPa
364 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.100 J/cm
0.187 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*3; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 72.0 J

@Temperature 23.0 °C
53.1 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 137 °C
279 °F
Rate B/50; ASTM D1525
140 °C
284 °F
Rate B/50; ISO 306
141 °C
286 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D542
1.586
1.586
ISO 489
Descriptive Properties Value Comments
Erichson scratch depth, 6N 17micrometer
SABIC Method
Pencil Hardness test, 1kgf HB
ASTM D3363