SABIC Innovative Plastics Lexan® 500 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 500 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LEXAN 500 resin grade is a medium viscosity, 10% glass reinforced, flame retardant product designed for applications requiring high rigidity together with high heat resistance and excellent impact performance.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.31 %
0.31 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 115 MPa
16700 psi
ISO 2039-1
Tensile Strength at Break 45.0 MPa
6530 psi
5 mm/min; ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
5 mm/min; ISO 527
Elongation at Break 7.0 %
7.0 %
5 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 3.30 GPa
479 ksi
1 mm/min; ISO 527
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
130 kJ/m²

@Temperature -30.0 °C
61.9 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²
7.14 ft-lb/in²
ISO 179/2C
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 11
11
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 132 °C
270 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 141 °C
286 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 1.47 mm
V-0

@Thickness 0.0579 in
UL 94 by SABIC-IP
5VA

@Thickness 3.05 mm
5VA

@Thickness 0.120 in
UL 94 by SABIC-IP
Oxygen Index 35 %
35 %
ISO 4589
Glow Wire Test 850 °C

@Thickness 1.00 mm
1560 °F

@Thickness 0.0394 in
IEC 60695-2-12
960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2