SABIC Innovative Plastics Lexan® 4404 PPC+PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyphthalate Carbonate
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 4404 PPC+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat polycarbonate copolymer, with HDT of 287F at 264 psi. FDA food contact compliant. Effective Jan 15th, 2008 this grade should not be used for medical applications which require biocompatibility. Alternative grade HPH4404This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.35 %
0.35 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %

@Temperature 23.0 °C
0.16 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
on tensile bar; SABIC Method
0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.00 - 0.0020 cm/cm

@Thickness 3.20 mm
0.00 - 0.0020 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
29 g/10 min

@Load 2.16 kg,
Temperature 330 °C
29 g/10 min

@Load 4.76 lb,
Temperature 626 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
70.0 MPa
10200 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break >= 50 %
>= 50 %
Type I, 50 mm/min; ASTM D 638
85 %
85 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.10 GPa
305 ksi
5 mm/min; ASTM D 638
2.15 GPa
312 ksi
1 mm/min; ISO 527
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D 790
100 MPa
14500 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 6.00 J/cm

@Temperature 23.0 °C
11.2 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
53.0 kJ/m²

@Temperature 23.0 °C
25.2 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.70 J/cm²

@Temperature 23.0 °C
27.1 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 120 J

@Temperature 23.0 °C
88.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 149 °C
300 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
148 °C

@Thickness 3.20 mm
298 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 155 °C
311 °F
Rate B/50; ISO 306
157 °C
315 °F
Rate B/120; ISO 306
166 °C
331 °F
Rate B/50; ASTM D 1525
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C pass
IEC 60695-10-2