SABIC Innovative Plastics Lexan® 193 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 193 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. UV-stabilized. Opaques only.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Water Absorption 0.19 %

@Time 86400 sec
0.19 %

@Time 24.0 hour
ASTM D 570
Moisture Absorption at Equilibrium 0.37 %

@Temperature 23.0 °C
0.37 %

@Temperature 73.4 °F
ASTM D 570
0.54 %

@Temperature 100 °C
0.54 %

@Temperature 212 °F
ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 68
68
ASTM D 785
Hardness, Rockwell R 118
118
ASTM D 785
Tensile Strength at Break 63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 115 %
115 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 81.0 MPa
11700 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.13 GPa
309 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 7.47 J/cm

@Temperature 23.0 °C
14.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 32.04 J/cm

@Temperature 23.0 °C
60.02 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Tensile Impact Strength 420 kJ/m²
200 ft-lb/in²
Type S; ASTM D 1822
Dart Drop, Total Energy 169 J

@Temperature 23.0 °C
125 ft-lb

@Temperature 73.4 °F
ASTM D 3029
Taber Abrasion, mg/1000 Cycles 20

@Load 1.00 kg
20

@Load 2.20 lb
CS-17; ASTM D 1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 64.8 µm/m-°C

@Temperature -40.0 - 95.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 6.40 mm
279 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C

@Thickness 6.40 mm
259 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 2.50e+17 ohm-cm
2.50e+17 ohm-cm
ASTM D 257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
ASTM D 150
Dielectric Strength 16.3 kV/mm

@Thickness 3.20 mm
414 kV/in

@Thickness 0.126 in
in air; ASTM D 149
Dissipation Factor 0.00090

@Frequency 50.0 - 60.0 Hz
0.00090

@Frequency 50.0 - 60.0 Hz
ASTM D 150
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM D 150