SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ASTM D 792
1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.2 %
1.2 %
23°C / 50% RH; ISO 62
0.85 %

@Time 86400 sec
 0.85 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0037 - 0.0057 cm/cm

@Time 86400 sec
 0.0037 - 0.0057 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
 0.010 - 0.012 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 118 MPa
17100 psi
Type I, 5 mm/min; ASTM D 638
125 MPa
18100 psi
5 mm/min; ISO 527
Tensile Strength, Yield 118 MPa
17100 psi
Type I, 5 mm/min; ASTM D 638
125 MPa
18100 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 6.23 GPa
904 ksi
1 mm/min; ISO 527
6.92 GPa
1000 ksi
50 mm/min; ASTM D 638
Flexural Strength 180 MPa
26100 psi
1.3 mm/min, 50 mm span; ASTM D 790
184 MPa
26700 psi
2 mm/min; ISO 178
Flexural Modulus 5.57 GPa
808 ksi
2 mm/min; ISO 178
6.54 GPa
949 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.950 J/cm

@Temperature -40.0 °C
 1.78 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
0.950 J/cm

@Temperature 23.0 °C
 1.78 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 6.02 J/cm

@Temperature 23.0 °C
 11.3 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -40.0 °C
 4.28 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 38.0 kJ/m²

@Temperature -40.0 °C
 18.1 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1U
41.0 kJ/m²

@Temperature 23.0 °C
 19.5 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 5.00 J

@Temperature 23.0 °C
 3.69 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.2 µm/m-°C

@Temperature -30.0 - 30.0 °C
 24.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM E 831
CTE, linear, Transverse to Flow 75.8 µm/m-°C

@Temperature -30.0 - 30.0 °C
 42.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 261 °C
502 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
261 °C

@Thickness 3.20 mm
 502 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
255 °C

@Thickness 3.20 mm
 491 °F

@Thickness 0.126 in
 unannealed; ASTM D 648