SABIC Innovative Plastics LNP Verton NV0081EV_GY7E149 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton NV0081EV_GY7E149 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
1.536 g/cc
0.05549 lb/in³
ASTM D 792
Water Absorption 0.070 %

@Temperature 23.0 °C,
Time 86400 sec
 0.070 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
0.057 %

@Time 86400 sec
 0.057 %

@Time 24.0 hour
 ASTM D 570
Linear Mold Shrinkage, Flow 0.00060 - 0.0026 cm/cm

@Time 86400 sec
 0.00060 - 0.0026 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0031 - 0.0051 cm/cm

@Time 86400 sec
 0.0031 - 0.0051 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 92.0 MPa
13300 psi
Type I, 5 mm/min; ASTM D 638
100 MPa
14500 psi
5 mm/min; ISO 527
Tensile Strength, Yield 92.0 MPa
13300 psi
Type I, 5 mm/min; ASTM D 638
100 MPa
14500 psi
5 mm/min; ISO 527
Elongation at Break 0.90 %
0.90 %
Type I, 5 mm/min; ASTM D 638
0.90 %
0.90 %
5 mm/min; ISO 527
1.2 %
1.2 %
Flexural Strain, 2 mm/min; ISO 178
Elongation at Yield 0.90 %
0.90 %
Type I, 5 mm/min; ASTM D 638
0.90 %
0.90 %
5 mm/min; ISO 527
Tensile Modulus 10.75 GPa
1559 ksi
1 mm/min; ISO 527
12.26 GPa
1778 ksi
50 mm/min; ASTM D 638
Flexural Strength 152 MPa
22000 psi
2 mm/min; ISO 178
156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 152 MPa
22000 psi
2 mm/min; ISO 178
156 MPa
22600 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 12.35 GPa
1791 ksi
2 mm/min; ISO 178
12.9 GPa
1870 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.45 J/cm

@Temperature 23.0 °C
 4.59 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
3.03 J/cm

@Temperature -40.0 °C
 5.68 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
Izod Impact, Unnotched 4.35 J/cm

@Temperature 23.0 °C
 8.15 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
4.77 J/cm

@Temperature -40.0 °C
 8.94 ft-lb/in

@Temperature -40.0 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 26.0 kJ/m²

@Temperature 23.0 °C
 12.4 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
29.0 kJ/m²

@Temperature -40.0 °C
 13.8 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 27.0 kJ/m²

@Temperature -40.0 °C
 12.8 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1U
32.0 kJ/m²

@Temperature 23.0 °C
 15.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 11.0 J

@Temperature 23.0 °C
 8.11 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 37.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
88.0 °C

@Thickness 3.20 mm
 190 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 - 1.60 mm
 V-0

@Thickness 0.0591 - 0.0630 in
 UL 94