SABIC Innovative Plastics LNP Verton NV0041EV_GY7E147 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton NV0041EV_GY7E147 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 20% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
1.373 g/cc
0.04960 lb/in³
ASTM D 792
Water Absorption 0.11 %

@Temperature 23.0 °C,
Time 86400 sec
 0.11 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
0.083 %

@Time 86400 sec
 0.083 %

@Time 24.0 hour
 ASTM D 570
Linear Mold Shrinkage, Flow 0.00060 - 0.0026 cm/cm

@Time 86400 sec
 0.00060 - 0.0026 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0034 - 0.0054 cm/cm

@Time 86400 sec
 0.0034 - 0.0054 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 99.0 MPa
14400 psi
Type I, 5 mm/min; ASTM D 638
105 MPa
15200 psi
5 mm/min; ISO 527
Tensile Strength, Yield 99.0 MPa
14400 psi
Type I, 5 mm/min; ASTM D 638
105 MPa
15200 psi
5 mm/min; ISO 527
Elongation at Break 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
1.7 %
1.7 %
5 mm/min; ISO 527
1.9 %
1.9 %
Flexural Strain, 2 mm/min; ISO 178
Elongation at Yield 1.5 %
1.5 %
Type I, 5 mm/min; ASTM D 638
1.7 %
1.7 %
5 mm/min; ISO 527
Tensile Modulus 7.03 GPa
1020 ksi
1 mm/min; ISO 527
7.64 GPa
1110 ksi
50 mm/min; ASTM D 638
Flexural Strength 139 MPa
20200 psi
1.3 mm/min, 50 mm span; ASTM D 790
141 MPa
20500 psi
2 mm/min; ISO 178
Flexural Yield Strength 139 MPa
20200 psi
1.3 mm/min, 50 mm span; ASTM D 790
141 MPa
20500 psi
2 mm/min; ISO 178
Flexural Modulus 7.25 GPa
1050 ksi
2 mm/min; ISO 178
8.19 GPa
1190 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.54 J/cm

@Temperature 23.0 °C
 2.89 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
1.94 J/cm

@Temperature -40.0 °C
 3.63 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
Izod Impact, Unnotched 3.04 J/cm

@Temperature 23.0 °C
 5.70 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
3.30 J/cm

@Temperature -40.0 °C
 6.18 ft-lb/in

@Temperature -40.0 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 16.0 kJ/m²

@Temperature 23.0 °C
 7.61 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
17.0 kJ/m²

@Temperature -40.0 °C
 8.09 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 21.0 kJ/m²

@Temperature 23.0 °C
 9.99 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
21.0 kJ/m²

@Temperature -40.0 °C
 9.99 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1U
Impact Test 8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 51.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 28.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
89.0 °C

@Thickness 3.20 mm
 192 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 - 1.60 mm
 V-0

@Thickness 0.0591 - 0.0630 in
 UL 94