SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ASTM D792
1.60 g/cc
0.0578 lb/in³
ISO 1183
Water Absorption 0.90 %

@Time 86400 sec
 0.90 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0018 cm/cm

@Time 86400 sec
 0.0018 in/in

@Time 24.0 hour
 ASTM D955
0.0030 cm/cm

@Time 86400 sec
 0.0030 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0022 cm/cm

@Time 86400 sec
 0.0022 in/in

@Time 24.0 hour
 ASTM D955
0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 254 MPa
36800 psi
ASTM D638
265 MPa
38400 psi
ISO 527
276 MPa
40000 psi
5 mm/min; ISO 527
Tensile Strength, Yield 276 MPa
40000 psi
5 mm/min; ISO 527
Elongation at Break 1.9 %
1.9 %
ASTM D638
1.9 %
1.9 %
ISO 527
2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 17.51 GPa
2540 ksi
50 mm/min; ASTM D638
17.8 GPa
2580 ksi
1 mm/min; ISO 527
Flexural Strength 370 MPa
53700 psi
ISO 178
374 MPa
54200 psi
ASTM D790
Flexural Yield Strength 366 MPa
53100 psi
2 mm/min; ISO 178
Flexural Modulus 14.16 GPa
2054 ksi
ASTM D790
15.0 GPa
2180 ksi
2 mm/min; ISO 178
15.55 GPa
2255 ksi
ISO 178
Izod Impact, Notched 3.84 J/cm
7.19 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1A
38.0 kJ/m²

@Temperature -40.0 °C
 18.1 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²
42.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 15.0 J
11.1 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 10.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
18.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 10.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 67.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
67.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 259 °C
498 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 256 °C
493 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
241 °C

@Thickness 3.20 mm
 466 °F

@Thickness 0.126 in
 unannealed; ASTM D648
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 110 °C
230 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 UL 94
Electrical Properties Metric English Comments
Hot Wire Ignition, HWI 0.00 - 2.0 sec
0.00 - 2.0 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A