SABIC Innovative Plastics LNP VERTON RV0079 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV0079 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* RV0079 is a compound based on Nylon 66 resin containing 35% Long Glasss Fiber. Added features of this material include: Flame Retardant, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.590 % | 0.590 % | 50% RH, 24 hrs; ASTM D570 |
| 0.750 % | 0.750 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 177 MPa | 25700 psi | 5 mm/min; ISO 527 |
| 194 MPa | 28100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 177 MPa | 25700 psi | 5 mm/min; ISO 527 |
| 194 MPa | 28100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.38 GPa | 1796 ksi | 1 mm/min; ISO 527 |
| 14.78 GPa | 2144 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 241 MPa | 35000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 241 MPa | 35000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.81 GPa | 1568 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.14 J/cm | 5.88 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.06 J/cm | 15.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 259 °C @Thickness 3.20 mm |
498 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.70 mm |
V-0 @Thickness 0.0669 in |
UL 94 by SABIC-IP |