SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermotuf* U1000AIS is a compound based on Polyphthalamide resin. Added features of this material include: High Impact, Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| 1.12 g/cc | 0.0405 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.017 cm/cm @Time 86400 sec |
0.017 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ISO 527 |
| 58.0 MPa | 8410 psi | ASTM D 638 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ISO 527 |
| 59.0 MPa | 8560 psi | ASTM D 638 | |
| Elongation at Break | 12.6 % | 12.6 % | ISO 527 |
| 17 % | 17 % | ASTM D 638 | |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D 638 |
| 7.3 % | 7.3 % | ISO 527 | |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.75 GPa | 399 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 79.0 MPa | 11500 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.06 GPa | 299 ksi | ASTM D 790 | |
| Izod Impact, Notched | 5.87 J/cm @Temperature 23.0 °C |
11.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 19.22 J/cm @Temperature 23.0 °C |
36.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 44.0 kJ/m² @Temperature 23.0 °C |
20.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 172 kJ/m² @Temperature 23.0 °C |
81.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 52.0 J | 38.4 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |