SABIC Innovative Plastics LNP Thermocomp ZF0041XC PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp ZF0041XC PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* ZF0041XC is a compound based on PPE+PS Blend resin containing Glass Fiber and Flame retardant. Added features include Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
5 mm/min; ISO 527
Elongation at Break 1.6 %
1.6 %
5 mm/min; ISO 527
Tensile Modulus 6.60 GPa
957 ksi
1 mm/min; ISO 527
Flexural Yield Strength 108 MPa
15700 psi
2 mm/min; ISO 178
Flexural Modulus 6.40 GPa
928 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 117 °C
243 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
 UL 94 by SABIC-IP