SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
2.7 specific gravity PBTThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 2.695 g/cc
0.09736 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.080 %

@Time 86400 sec
0.080 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0069 - 0.0089 cm/cm

@Time 86400 sec
0.0069 - 0.0089 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
5 mm/min; ISO 527
31.0 MPa
4500 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 31.0 MPa
4500 psi
Type I, 5 mm/min; ASTM D 638
31.0 MPa
4500 psi
5 mm/min; ISO 527
Elongation at Break 0.70 %
0.70 %
Type I, 5 mm/min; ASTM D 638
0.70 %
0.70 %
5 mm/min; ISO 527
0.80 %
0.80 %
Flexural Strain, 2 mm/min; ISO 178
Elongation at Yield 0.50 %
0.50 %
Type I, 5 mm/min; ASTM D 638
0.50 %
0.50 %
5 mm/min; ISO 527
Tensile Modulus 8.28 GPa
1200 ksi
1 mm/min; ISO 527
10.46 GPa
1517 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 52.0 MPa
7540 psi
2 mm/min; ISO 178
56.0 MPa
8120 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 8.32 GPa
1210 ksi
1.3 mm/min, 50 mm span; ASTM D 790
8.32 GPa
1210 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.190 J/cm

@Temperature 23.0 °C
0.356 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 1.50 J/cm

@Temperature 23.0 °C
2.81 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 3.00 J

@Temperature 23.0 °C
2.21 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.3 - 45.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
24.1 - 25.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E 831
CTE, linear, Transverse to Flow 57.5 - 59.5 µm/m-°C

@Temperature -30.0 - 30.0 °C
31.9 - 33.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
164 °C

@Thickness 3.20 mm
327 °F

@Thickness 0.126 in
unannealed; ASTM D 648