SABIC Innovative Plastics LNP Thermocomp WFB51 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp WFB51 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* WFB51 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Glass Fiber. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| 1.514 g/cc | 0.05470 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0129 cm/cm @Time 86400 sec |
0.0129 in/in @Time 24.0 hour |
ISO 294 |
| 0.013 cm/cm @Time 86400 sec |
0.013 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0158 cm/cm @Time 86400 sec |
0.0158 in/in @Time 24.0 hour |
ISO 294 |
| 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D 638 |
| 58.0 MPa | 8410 psi | ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D 638 |
| 3.2 % | 3.2 % | ISO 527 | |
| Tensile Modulus | 4.20 GPa | 609 ksi | 50 mm/min; ASTM D 638 |
| 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| 101 MPa | 14600 psi | ASTM D 790 | |
| Flexural Modulus | 4.12 GPa | 598 ksi | ISO 178 |
| 4.13 GPa | 599 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.260 J/cm @Temperature 23.0 °C |
0.487 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.83 J/cm @Temperature 23.0 °C |
5.30 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
Users viewing this material also viewed the following:
- Polymer Resources NY66-GP1-[color]H Nylon, General Purpose Heat Stabilized (DAM)
- SABIC PP 674K Polypropylene Copolymer for Injection Molding
- DuPont Bynel® 3062 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 80-7489 Polyacetal-copolymer, with carbon fiber
- Lubriplate FMO 500 AW USP Mineral Oil-Based Food Machinery Grade Oil
- A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 100 Gauge
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.25 PHR Zinc Stearate
- Radici Radilon® S 38F (dry) Nylon 6
- Axiall 22882 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved