SABIC Innovative Plastics LNP Thermocomp RFB53U PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RFB53U PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP*THERMOCOMP*RFB53U is a compound based on PA 66 resin containing Glass Bead, Glass Fiber. Added features include: UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 201 MPa | 29200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 86.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Kingfa JH720 G20 20% Glass Fiber Reinforced PC
- Gouda Vuurvast AK 85 K Dense Refractory Brick
- Lubrizol Advanced Materials Pearlstick® 45-90/12 Polycaprolactone based TPU
- Samyang Tribit® 1500A15 PBT, Inorganic Reinforced
- Polyplastics Duranex® 353RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 30% GF filled
- Ecomass® 1003ZD95 Tungsten Filled COPA
- Wellman Wellamid® FRGF1850-N1 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved