SABIC Innovative Plastics LNP Thermocomp RF00CS PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp RF00CS PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RF00CS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D 792 |
| 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec |
0.0029 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0044 cm/cm @Time 86400 sec |
0.0044 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 253 MPa | 36700 psi | ASTM D 638 |
| 253 MPa | 36700 psi | ISO 527 | |
| Tensile Strength, Yield | 253 MPa | 36700 psi | ASTM D 638 |
| 253 MPa | 36700 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D 638 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D 638 | |
| Tensile Modulus | 21.36 GPa | 3098 ksi | 1 mm/min; ISO 527 |
| 21.37 GPa | 3099 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 358 MPa | 51900 psi | ASTM D 790 |
| 375 MPa | 54400 psi | ISO 178 | |
| Flexural Modulus | 19.3 GPa | 2800 ksi | ASTM D 790 |
| 20.0 GPa | 2900 ksi | ISO 178 | |
| Izod Impact, Notched | 1.60 J/cm @Temperature 23.0 °C |
3.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 12.28 J/cm @Temperature 23.0 °C |
23.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² @Temperature 23.0 °C |
36.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 16.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
8.89 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 16.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
9.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PA1501 Polyamide 66 - Carbon Nanotube Masterbatch
- LATI LARPEEK 50 K/30 30% Carbon Fiber Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Nilit Nilamid B G6 FR C4 30% Glass Fiber Reinforced, Flame Retardant PA6
- Lubriplate SYN SYN-1600 PAO-Based Multi-Purpose Grease
- H.C. Starck Amperit® 413.6 Gas Atomized (NiCoCrAlY)
- Shin-Etsu Silicones KE-5570U Low Temperature Silicone Elastomer
- Vyncolit Neopreg Kinel® SK80 L8G Glass Fiber Reinforced Molding Compound
- Fainplast Compounds HGK 83 Flexible PVC, Sheathing for High Temperatures Lead Free
- 3M FM021 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- Polyplastics Duracon® HP25X Acetal Co-polymer (POM), High stiffness, High viscosity
Copyright © lookpolymers.com All Rights Reserved