SABIC Innovative Plastics LNP Thermocomp RF00AES PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp RF00AES PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* RF00AES is a compound based on PA66 resin containing Glass Fiber, Mold Release.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.85 %
0.85 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 2.75 %

@Temperature 23.0 °C
 2.75 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
on tensile bar; SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell L 114
114
ISO 2039-2
Tensile Strength at Break 210 MPa
30500 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 16.0 GPa
2320 ksi
1 mm/min; ISO 527
Flexural Strength 310 MPa
45000 psi
2 mm/min; ISO 178
Flexural Modulus 15.0 GPa
2180 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature -20.0 °C
 5.71 ft-lb/in²

@Temperature -4.00 °F
 80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 6.67 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 136 µm/m-°C

@Temperature 23.0 - 60.0 °C
 75.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 235 °C
455 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 230 °C
446 °F
Rate B/50; ISO 306
232 °C
450 °F
Rate B/120; ISO 306
240 °C
464 °F
Rate A/50; ISO 306
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 UL 94
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 2nd value; UL 94
Oxygen Index 27 %
27 %
LOI; ISO 4589
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.4

@Frequency 50.0 - 60.0 Hz
 3.4

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 19.0 kV/mm

@Thickness 3.20 mm
 483 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.0068

@Frequency 50.0 - 60.0 Hz
 0.0068

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index >= 350 V
>= 350 V
IEC 60112
500 V
500 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2