SABIC Innovative Plastics LNP Thermocomp RB008 PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp RB008 PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* RB008 is a compound based on PA 66 resin containing Glass Bead.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 83.0 MPa
12000 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527
Tensile Modulus 5.20 GPa
754 ksi
1 mm/min; ISO 527
Flexural Yield Strength 128 MPa
18600 psi
2 mm/min; ISO 178
Flexural Modulus 4.40 GPa
638 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 58.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 32.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 57.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 31.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af