SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PH0600A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 5.90 g/cc | 5.90 g/cc | ASTM D 792 |
| Density | 5.90 g/cc | 0.213 lb/in³ | ISO 1183 |
| 6.00 g/cc | 0.217 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Time 86400 sec |
0.0060 - 0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D 638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.50 % | 0.50 % | Type I, 5 mm/min; ASTM D 638 |
| 0.50 % | 0.50 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.11 GPa | 1611 ksi | 1 mm/min; ISO 527 |
| 14.98 GPa | 2173 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 81.0 MPa | 11700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 96.0 MPa | 13900 psi | ASTM D 790 | |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 9.78 GPa | 1420 ksi | 2 mm/min; ISO 178 |
| 9.79 GPa | 1420 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 11.5 GPa | 1670 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.41 J/cm @Temperature 23.0 °C |
2.64 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 38.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 196 °C | 385 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 169 °C @Thickness 3.20 mm |
336 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |