SABIC Innovative Plastics LNP Thermocomp PFB42U PA 6 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp PFB42U PA 6 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STARAMIDE PFB42U is a compound based on Nylon 6 resin containing Glassfiber and Glass Beads Additional features include Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527
Flexural Strength 140 MPa
20300 psi
2 mm/min; ISO 178
Flexural Modulus 4.40 GPa
638 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 170 °C

@Treatment Temp. 120 °C,
Time 7200 sec
 338 °F

@Treatment Temp. 248 °F,
Time 2.00 hour
 annealed; ISO 75/Ae
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 UL 94 by SABIC-IP