SABIC Innovative Plastics LNP Thermocomp M10009A PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp M10009A PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STARFLAM* M10009A is a compound based on Polypropylene resin, containing Flame Retardant. Added features include : Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Temperature 23.0 °C, Time 86400 sec |
0.010 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm | 0.016 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 7.3 % | 7.3 % | 50 mm/min; ISO 527 |
| Flexural Yield Strength | 50.0 MPa | 7250 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 106 µm/m-°C @Temperature 23.0 - 60.0 °C |
58.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 60.0 °C |
77.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- RheTech Products G13P100-553UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 501F) Dark Smoke Gray
- Polymax® Maxelast® P1855 TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Lexan® ML6413 PC
- Kazanorgsintez 276-288 High Density Polyethylene Composite
- Lubrizol ESTANE® T5192 Ether-Type Dissipative Compound (European Grade)
- A. Schulman POLYBATCH™ Red 5505 Concentrate Based In Polyethylene
- Eurotec® Tecomid® NT40 NL XA60 PPA, unfilled, flame retardant - halogen & red phosphorus free, heat stabilized, natural
- Fainplast Compounds GA 87/4 Flexible PVC, Flame Retardant Sheathing
- Akro-Plastic Akromid® S3 GF 23 1 (2917) PA 6.10 Conditioned, 23% Glass Filled
Copyright © lookpolymers.com All Rights Reserved