SABIC Innovative Plastics LNP Thermocomp FF004 PE (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp FF004 PE (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* FF004 is a compound based on Polyethylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 0.010 %

@Temperature 23.0 °C,
Time 86400 sec
 0.010 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa
6670 psi
5 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
Flexural Yield Strength 60.0 MPa
8700 psi
2 mm/min; ISO 178
Flexural Modulus 3.10 GPa
450 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 25.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 162 µm/m-°C

@Temperature 23.0 - 60.0 °C
 90.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af