SABIC Innovative Plastics LNP Thermocomp DFZ22E PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp DFZ22E PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.35 g/cc
1.35 g/cc
ASTM D 792
Moisture Absorption at Equilibrium 0.14 %
0.14 %
23°C / 50% RH; ISO 62
0.13 %

@Time 86400 sec
0.13 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
Type I, 5 mm/min; ASTM D 638
72.0 MPa
10400 psi
5 mm/min; ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
Type I, 5 mm/min; ASTM D 638
75.0 MPa
10900 psi
5 mm/min; ISO 527
Elongation at Break 4.5 %
4.5 %
5 mm/min; ISO 527
5.0 %
5.0 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.1 %
3.1 %
5 mm/min; ISO 527
3.3 %
3.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 4.96 GPa
719 ksi
1 mm/min; ISO 527
5.12 GPa
743 ksi
50 mm/min; ASTM D 638
Flexural Strength 130 MPa
18900 psi
ISO 178
Flexural Yield Strength 132 MPa
19100 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 4.42 GPa
641 ksi
1.3 mm/min, 50 mm span; ASTM D 790
4.44 GPa
644 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.730 J/cm

@Temperature 23.0 °C
1.37 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 8.21 J/cm

@Temperature 23.0 °C
15.4 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²

@Temperature 23.0 °C
25.2 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
15.0 J

@Temperature 23.0 °C
11.1 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 4.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
2.22 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
144 °C

@Thickness 3.20 mm
291 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D 648