SABIC Innovative Plastics LNP THERMOCOMP VC006 SUPER TOUGH NYLON
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP VC006 SUPER TOUGH NYLON.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOTUF* VC006 is a compound based on Super Tough Nylon resin containing 30% Carbon Fiber. Added features of this material include: High Impact, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.620 % | 0.620 % | 50% RH, 24 hrs; ASTM D570 |
| 0.950 % | 0.950 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 193 MPa | 28000 psi | 5 mm/min; ISO 527 |
| 197 MPa | 28600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 193 MPa | 28000 psi | 5 mm/min; ISO 527 |
| 197 MPa | 28600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 19.34 GPa | 2805 ksi | 1 mm/min; ISO 527 |
| 20.7 GPa | 3000 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 284 MPa | 41200 psi | ISO 178 |
| 286 MPa | 41500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 293 MPa | 42500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 15.3 GPa | 2220 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 15.53 GPa | 2252 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 2.07 J/cm | 3.88 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.7 J/cm | 20.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 32.0 J @Temperature 23.0 °C |
23.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 102 µm/m-°C @Temperature -30.0 - 30.0 °C |
56.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Owens Corning Glass Fiber Reinforced Polystyrene Acrylonitrile (SAN), 20 wt.% glass
- Fiberfil® PP-60/TC/40 Polypropylene Homopolymer, 40% Talc Filled
- Mitsubishi Xantar® F 22 R Polycarbonate
- Chase Plastics CP Pryme® PC100RUV Polycarbonate, Mold Release, UV Stabilized
- Dow 5D49 Polypropylene Homopolymer Resin
- A. Schulman ComAlloy Hiloy® 514 Polycarbonate, Glass Reinforced, UL
- 3M 4014/Silver Damping Foils
- 3M 7983 Sheet Polyester Label Material
- Adell ZR-17 33% Glass Reinforced Nylon/Olefin Alloy
Copyright © lookpolymers.com All Rights Reserved