SABIC Innovative Plastics LNP THERMOCOMP UX06003 PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UX06003 PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* UX06003 is a compound based on Polyphalamide resin containing Carbon Fiber. Added features include Electrically Conductive, Mold Release, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 275 MPa | 39900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.6 GPa | 1830 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 353 MPa | 51200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
6.67 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
35.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FCC-216-P High Carbon Copper Steel Powdered Metal
- H.C. Starck Amperit® 519.088 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F)
- SABIC Innovative Plastics NORYL EM6101 PPE+PS
- Westlake Plastics Zelux® SD-P Polycarbonate (static dissipative)
- DuPont Performance Polymers Delrin® 500CL BK601 Acetal (POM) (Unverified Data**)
- BASF N-Ethylpyrrolidone-2 (NEP)
- Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded
- REXtac Rextac® RT 5224 Amorphous Polyalphaolefin (APAO)
Copyright © lookpolymers.com All Rights Reserved