SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP UF0067W PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* UF0067W is a compound based on Polyphthalamide resin containing 30% glass fiber. Added features of this material include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flame Retardant.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ASTM D792
1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm

@Time 86400 sec
 0.0020 - 0.0050 in/in

@Time 24.0 hour
 ASTM D955
0.0020 - 0.0050 cm/cm

@Time 86400 sec
 0.0020 - 0.0050 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm

@Time 86400 sec
 0.012 - 0.015 in/in

@Time 24.0 hour
 ASTM D955
0.012 - 0.015 cm/cm

@Time 86400 sec
 0.012 - 0.015 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 128 MPa
18600 psi
5 mm/min; ISO 527
143 MPa
20700 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.9 %
1.9 %
5 mm/min; ISO 527
2.5 %
2.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 10.54 GPa
1529 ksi
5 mm/min; ASTM D638
11.31 GPa
1640 ksi
1 mm/min; ISO 527
Flexural Strength 189 MPa
27400 psi
ISO 178
213 MPa
30900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 9.13 GPa
1320 ksi
2 mm/min; ISO 178
10.2 GPa
1480 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.62 J/cm
12.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 28.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
51.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 28.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 299 °C

@Thickness 3.20 mm
 570 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
281 °C

@Thickness 3.20 mm
 538 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Electrical Properties Metric English Comments
Dielectric Constant 3.82

@Frequency 1.00e+6 Hz
 3.82

@Frequency 1.00e+6 Hz
 ASTM D150
4.05

@Frequency 1000 Hz
 4.05

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 29.7 kV/mm

@Thickness 0.800 mm
 754 kV/in

@Thickness 0.0315 in
 in oil; ASTM D149
Dissipation Factor 0.0115

@Frequency 1000 Hz
 0.0115

@Frequency 1000 Hz
 ASTM D150
0.0128

@Frequency 1.00e+6 Hz
 0.0128

@Frequency 1.00e+6 Hz
 ASTM D150