SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0450C PUR (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* TH0450C is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.50 g/cc | 0.163 lb/in³ | ASTM D792 |
| 4.50 g/cc | 0.163 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0057 cm/cm @Time 86400 sec |
0.0057 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0057 cm/cm @Time 86400 sec |
0.0057 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| 13.0 MPa | 1890 psi | ISO 527 | |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| 16.0 MPa | 2320 psi | ISO 527 | |
| Elongation at Break | 23.1 % | 23.1 % | ISO 527 |
| 27.3 % | 27.3 % | ASTM D638 | |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527 |
| 8.5 % | 8.5 % | ASTM D638 | |
| Tensile Modulus | 1.17 GPa | 170 ksi | 1 mm/min; ISO 527 |
| 1.33 GPa | 193 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| 21.0 MPa | 3050 psi | ISO 178 | |
| Flexural Modulus | 0.990 GPa | 144 ksi | ASTM D790 |
| 1.13 GPa | 164 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 17.0 J | 12.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 12.0 J | 8.85 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 78.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 46.0 °C @Thickness 3.20 mm |
115 °F @Thickness 0.126 in |
unannealed; ASTM D648 |