SABIC Innovative Plastics LNP THERMOCOMP SF006 PA 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SF006 PA 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* SF006 is a compound based on Nylon 12 resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| 1.243 g/cc | 0.04491 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Time 86400 sec |
0.0020 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0021 - 0.0030 cm/cm @Time 86400 sec |
0.0021 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0080 cm/cm @Time 86400 sec |
0.0070 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0074 - 0.0081 cm/cm @Time 86400 sec |
0.0074 - 0.0081 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
| 108 MPa | 15700 psi | ISO 527 | |
| Elongation at Break | 4.6 % | 4.6 % | ISO 527 |
| 4.7 % | 4.7 % | ASTM D638 | |
| Tensile Modulus | 6.55 GPa | 950 ksi | 50 mm/min; ASTM D638 |
| 6.58 GPa | 954 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 169 MPa | 24500 psi | ISO 178 |
| 170 MPa | 24700 psi | ASTM D790 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| 6.24 GPa | 905 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 43.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 113 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N90M Nitrile Rubber
- Momentive Performance Materials Siloprenâ„¢ LSR 7060 High Clarity Liquid Silicone Rubber
- Stir SpA Giesse EPM/75 (PVC)
- Shinkong Synthetic Fibers Shinite® P305G20 PP, 20% Glass Filled
- Struktol V-PEAS Processing Additive
- Vyncolit X620/1 Novolac Phenolic
- A. Schulman POLYBATCH™ Yellow LL20203/2 Concentrate Based In LDPE
- ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin (European Grade)
- BASF Neopolen® P 9230 D 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- 3M 7744 Polyester Overlaminating Film
Copyright © lookpolymers.com All Rights Reserved