SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.750 % | 0.750 % | 50% RH, 24 hrs; ASTM D570 |
| 1.20 % | 1.20 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 181 MPa | 26300 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.55 GPa | 1530 ksi | 1 mm/min; ISO 527 |
| 11.0 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 264 MPa | 38300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.48 GPa | 1370 ksi | 2 mm/min; ISO 178 |
| 9.62 GPa | 1400 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.920 J/cm | 1.72 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.69 J/cm | 18.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 57.0 kJ/m² | 27.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 104 µm/m-°C @Temperature -30.0 - 30.0 °C |
57.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 243 °C @Thickness 3.20 mm |
469 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Lanxess Pocan® DP 4035 000000 PBT + PET, 30% Glass Fiber
- Solvay Specialty Polymers Udel® P-1710 Polysulfone (PSU)
- Polyram PlusTek PB840 Nylon 6, Impact Modified
- Crucible Steel 430 Chromium Steel
- Fainplast Compounds GS 7512 Flexible PVC, Injection Molding for Footwear
- 3M FV1172 Removable White Vinyl Label Products
- 3M Bumpon™ SJ6232 Resilient Rollstock
- 3M FV0146N Soft Clear Vinyl Label Products
- LyondellBasell Alathon® 9301 High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved