SABIC Innovative Plastics LNP THERMOCOMP RFM-3353 EM PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP RFM-3353 EM PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* RFM-3353 EM is a compound based on Nylon 66 resin containing Glass Fiber, Mineral. Added features of this material include: Easy Molding.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 119 MPa
17300 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 10.4 GPa
1510 ksi
1 mm/min; ISO 527
Flexural Strength 171 MPa
24800 psi
2 mm/min; ISO 178
Flexural Modulus 8.50 GPa
1230 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 71.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 39.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 248 °C
478 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 221 °C
430 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af