SABIC Innovative Plastics LNP THERMOCOMP RF006XXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006XXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF006XXH is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.640 % | 0.640 % | 50% RH, 24 hrs; ASTM D570 |
| 0.940 % | 0.940 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| 167 MPa | 24200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.57 GPa | 1533 ksi | 1 mm/min; ISO 527 |
| 11.42 GPa | 1656 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 233 MPa | 33800 psi | ISO 178 |
| 242 MPa | 35100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 9.40 GPa | 1360 ksi | 2 mm/min; ISO 178 |
| 9.70 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
15.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 98.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 246 °C @Thickness 3.20 mm |
475 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® S3000-S2.5N Silver-Coated Solid Glass Spheres
- SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer
- SABIC Innovative Plastics Lexan® ML6411 PC Copolymer
- RheTech Products M25P251-01 25% Mica Reinforced Polypropylene Copolymer, Black
- Iran Petrochemical (PCC) EP-C 30 R Polypropylene
- Teknor Apex APEX® 3201-70 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® SR-0300 Heat Resistant Grade ABS
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- A. Schulman SUPERLINEAR™ XL 0370 Rotational Molding Resin
Copyright © lookpolymers.com All Rights Reserved