SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.670 % | 0.670 % | 50% RH, 24 hrs; ASTM D570 |
| 0.990 % | 0.990 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 194 MPa | 28100 psi | 5 mm/min; ISO 527 |
| 200 MPa | 29000 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 195 MPa | 28300 psi | 5 mm/min; ISO 527 |
| 200 MPa | 29000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 |
| 3.3 % | 3.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.73 GPa | 1556 ksi | 1 mm/min; ISO 527 |
| 11.42 GPa | 1656 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 279 MPa | 40500 psi | ISO 178 |
| 286 MPa | 41500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 286 MPa | 41500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.25 GPa | 1340 ksi | 2 mm/min; ISO 178 |
| 9.51 GPa | 1380 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.34 J/cm | 2.51 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.8 J/cm | 24.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 82.0 kJ/m² | 39.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 32.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 64.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 251 °C @Thickness 3.20 mm |
484 °F @Thickness 0.126 in |
unannealed; ASTM D648 |