SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.860 % | 0.860 % | 50% RH, 24 hrs; ASTM D570 |
| 1.40 % | 1.40 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 |
| 137 MPa | 19900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 136 MPa | 19700 psi | Type I, 5 mm/min; ASTM D638 |
| 139 MPa | 20200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.79 GPa | 1420 ksi | 50 mm/min; ASTM D638 |
| 9.84 GPa | 1430 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 207 MPa | 30000 psi | ISO 178 | |
| 207 MPa | 30000 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | 2 mm/min; ISO 178 |
| 8.64 GPa | 1250 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.610 J/cm | 1.14 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.26 J/cm | 13.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 79.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 248 °C | 478 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 249 °C @Thickness 3.20 mm |
480 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 229 °C @Thickness 3.20 mm |
444 °F @Thickness 0.126 in |
unannealed; ASTM D648 |