SABIC Innovative Plastics LNP THERMOCOMP RF002ES PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF002ES PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF002ES is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| 1.224 g/cc | 0.04422 lb/in³ | ASTM D792 | |
| Moisture Absorption | 1.26 % | 1.26 % | 50% RH, 24 hrs; ASTM D570 |
| 1.94 % | 1.94 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0077 cm/cm @Time 86400 sec |
0.0077 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 87.0 MPa | 12600 psi | ASTM D638 |
| 90.0 MPa | 13100 psi | ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 |
| 2.5 % | 2.5 % | ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | ISO 527 |
| Tensile Modulus | 4.85 GPa | 703 ksi | 50 mm/min; ASTM D638 |
| 5.12 GPa | 743 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 131 MPa | 19000 psi | ISO 178 |
| 156 MPa | 22600 psi | ASTM D790 | |
| Flexural Modulus | 4.28 GPa | 621 ksi | ISO 178 |
| 4.61 GPa | 669 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 21.0 kJ/m² | 9.99 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 172 °C @Thickness 3.20 mm |
342 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymer Resources PC-IM1-UV Polycarbonate, Impact Modified, Low Flow, UV-stabilized
- Chevron Phillips EB6025 HIPS - High Impact Polystyrene (discontinued **)
- LyondellBasell Montell SE191 Polypropylene Impact Copolymer
- SABIC Innovative Plastics ULTEM 2100 PEI (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
- DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer
- Entec Hypro™ PPC-T40 Copolymer Polypropylene, 40% Talc Reinforced
- DuPont Elvax® 3200-2 Ethylene-Vinyl Acetate Copolymer Resin for Extrusion Coating
- Multibase Multi-Flam™ 0107 HDPE Polyethylene
Copyright © lookpolymers.com All Rights Reserved