SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF002 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF002 is a compound based on Nylon 66 resin containing 10% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| 1.215 g/cc | 0.04389 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| 1.70 % | 1.70 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0076 cm/cm @Time 86400 sec |
0.0076 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 |
| 112 MPa | 16200 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.6 % | 2.6 % | ASTM D638 | |
| Tensile Modulus | 5.24 GPa | 760 ksi | 1 mm/min; ISO 527 |
| 5.97 GPa | 866 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 139 MPa | 20200 psi | ISO 178 |
| 188 MPa | 27300 psi | ASTM D790 | |
| Flexural Modulus | 4.58 GPa | 664 ksi | ISO 178 |
| 5.37 GPa | 779 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.96 J/cm | 9.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C @Thickness 3.20 mm |
509 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 250 °C @Thickness 3.20 mm |
482 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC 318B Linear Low Density Polyethylene for Cast Film
- SABIC Innovative Plastics Cycolac® GRM2600L ABS
- Radici Radilon® CS 38FL (cond.) Nylon 6/66
- PolyOne Edgetek® SF-30GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
- KB Alloys 25% Magnesium Aluminum Alloy
- Teknor Apex Telcar® OBC 4876N Thermoplastic Elastomer
- A. Schulman COMTUF® 5011 10% Glass Fiber Reinforced Polycarbonate
- DuPont Elvaloy® 2116 AC Ethylene and 16% Ethyl Acrylate Copolymer
- Polyram RamSter PF310G6 PBT Alloy, 30% Glass Fiber, UV Stabilized
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
Copyright © lookpolymers.com All Rights Reserved