SABIC Innovative Plastics LNP THERMOCOMP QC006 PA6.10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP QC006 PA6.10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* QC006 is a compound based on Nylon 6/10 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 214 MPa | 31000 psi | Type I, 5 mm/min; ASTM D638 |
| 243 MPa | 35200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 23.01 GPa | 3337 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 325 MPa | 47100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 349 MPa | 50600 psi | ISO 178 | |
| Flexural Yield Strength | 326 MPa | 47300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 16.1 GPa | 2340 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 18.77 GPa | 2722 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.04 J/cm | 1.95 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.20 J/cm | 17.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
6.67 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Panjin Zhongrun Chemerize 085P Low Viscosity CoPEEK
- Lehmann & Voss LUVOCOM® 20-0665 Polyphthalamide, with carbon fiber, PTFE, lubricant modified
- Huntsman MY 9634 Multifunctional Resin
- Karina 42/154-FC-LMP (SDB) Red Color Concentrate for PVC
- Solvay MIRAPOL® SURF S 500 Surfactant
- Borealis Superclean™ LE4201EHV Polyethylene Insulation Compound, Crosslinkable
- Chicago Extruded Metals BioBrass® UNS C46400 Copper-Zinc-Tin Alloy
- Eurostar Staramide A28 PA66, Injection Molding
- ConocoPhillips Hydroclear® MV46 AW Hydraulic Fluid
- 3M Cold Seal® 3130 Polyethylene Tape
Copyright © lookpolymers.com All Rights Reserved