SABIC Innovative Plastics LNP THERMOCOMP PH1000A PA 6

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP PH1000A PA 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* PH1000A is a compound based on Nylon 6 resin. Added features of this material include: High Specific Gravity.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0072 cm/cm
0.0072 in/in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0074 cm/cm
0.0074 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
ASTM D638
Elongation at Break 0.40 %
0.40 %
ASTM D638
Tensile Modulus 16.45 GPa
2386 ksi
50 mm/min; ASTM D638
Flexural Strength 91.0 MPa
13200 psi
ASTM D790
Flexural Modulus 18.97 GPa
2751 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.60 J/cm
3.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 165 °C

@Thickness 3.20 mm
 329 °F

@Thickness 0.126 in
 unannealed; ASTM D648