SABIC Innovative Plastics LNP THERMOCOMP PF009 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PF009 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* PF009 is a compound based on Nylon 6 resin containing 45% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.870 % | 0.870 % | 50% RH, 24 hrs; ASTM D570 |
| 1.07 % | 1.07 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 192 MPa | 27800 psi | ASTM D638 |
| 201 MPa | 29200 psi | ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| 3.4 % | 3.4 % | ISO 527 | |
| Tensile Modulus | 14.53 GPa | 2107 ksi | 50 mm/min; ASTM D638 |
| 15.21 GPa | 2206 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 293 MPa | 42500 psi | ASTM D790 |
| 310 MPa | 45000 psi | ISO 178 | |
| Flexural Modulus | 10.55 GPa | 1530 ksi | ASTM D790 |
| 11.63 GPa | 1687 ksi | ISO 178 | |
| Izod Impact, Notched | 1.54 J/cm | 2.89 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 94.0 kJ/m² | 44.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 24.0 J | 17.7 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 20.0 J | 14.8 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs HO400 HoCl3·6H2O Holmium chloride hexahydrate
- Quadrant EPP Ketron® CLASSIX™ LSG PEEK LSG grade, extruded (ISO Data)
- Radici Radilon® S RV200 (dry) Nylon 6
- M. Holland Company CP402 Polypropylene Impact Copolymer
- SABIC Innovative Plastics ULTEM 2210EPR PEI
- Teknor Apex TEKBOND® 6000-60 Thermoplastic Elastomer
- DSM Stanyl® TE250F8 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Cond)
- CMT Materials HYTAC® B1X High Durability Thermoplastic Syntactic
- Akzo Nobel Expancel® 092 DU 120 Dry unexpanded microspheres
- Braskem F2523 Blown Film Extrusion Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved