SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP OF008E PPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* OF008E is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Time 86400 sec
0.0020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 160 MPa
23200 psi
ISO 527
178 MPa
25800 psi
ASTM D638
Elongation at Break 1.2 %
1.2 %
ISO 527
1.7 %
1.7 %
ASTM D638
Flexural Strength 190 MPa
27600 psi
ISO 178
248 MPa
36000 psi
ASTM D790
Flexural Modulus 13.4 GPa
1940 ksi
ISO 178
14.26 GPa
2068 ksi
ASTM D790
Izod Impact, Notched 1.01 J/cm
1.89 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.87 J/cm
11.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1U
Coefficient of Friction, Dynamic 0.66
0.66
ASTM D3702 Modified
Coefficient of Friction, Static 0.87
0.87
ASTM D3702 Modified
K (wear) Factor 483 x 10-8 mm³/N-M
240 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 272 °C
522 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
261 °C

@Thickness 3.20 mm
502 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.450 mm
V-0

@Thickness 0.0177 in
UL 94 by SABIC-IP