SABIC Innovative Plastics LNP THERMOCOMP NX11302 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NX11302 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC/ABS compound with colorable, good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 260 °C |
14 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 75 % | 75 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.23 GPa | 323 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.94 @Frequency 1.00e+9 Hz |
2.94 @Frequency 1.00e+9 Hz |
IEC 60250 |
| Dissipation Factor | 0.0057 @Frequency 1.00e+9 Hz |
0.0057 @Frequency 1.00e+9 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- MV Labs CU700 Cu(NO3)2·3H2O Copper(II) nitrate trihydrate
- Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA) (Unverified Data**)
- Shell Carilon® D26CX100 Polyketone, Advanced Extrusion Grade (discontinued **)
- Covestro Apec® DP9-9354 High-Heat Polycarbonate, Flame-Retardant (discontinued **)
- Plenco 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **)
- Kazanorgsintez E-15 Petroleum Resin
- I. Stern 750 Medium Impact Black ABS
- SABIC Innovative Plastics LNP THERMOCOMP BFL2200 PC (Asia Pacific)
- Eagle Brass 770 Nickel Silver 18%, Annealed
- CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved