SABIC Innovative Plastics LNP THERMOCOMP MH0400A PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MH0400A PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* MH0400A is a compound based on Polypropylene resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.00 g/cc | 0.145 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0101 cm/cm @Time 86400 sec |
0.0101 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Elongation at Yield | 1.8 % | 1.8 % | ISO 527 |
| Tensile Modulus | 6.59 GPa | 956 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 36.0 MPa | 5220 psi | ISO 178 |
| Flexural Modulus | 9.58 GPa | 1390 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |