SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
Physical Properties Metric English Comments
Specific Gravity 0.960 g/cc
0.960 g/cc
ASTM D792
Density 0.960 g/cc
0.0347 lb/in³
ASTM D792
Moisture Absorption 0.0200 %
0.0200 %
50% RH, 24 hrs; ASTM D570
0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
Type I, 5 mm/min; ASTM D638
35.0 MPa
5080 psi
5 mm/min; ISO 527
45.0 MPa
6530 psi
ASTM D638
Tensile Strength, Yield 41.0 MPa
5950 psi
5 mm/min; ISO 527
43.0 MPa
6240 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.7 %
3.7 %
ASTM D638
4.9 %
4.9 %
5 mm/min; ISO 527
5.4 %
5.4 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.4 %
3.4 %
Type I, 5 mm/min; ASTM D638
3.4 %
3.4 %
5 mm/min; ISO 527
Tensile Modulus 2.84 GPa
412 ksi
1 mm/min; ISO 527
3.25 GPa
471 ksi
50 mm/min; ASTM D638
Flexural Strength 58.0 MPa
8410 psi
ISO 178
68.0 MPa
9860 psi
ASTM D790
Flexural Yield Strength 66.0 MPa
9570 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.37 GPa
344 ksi
2 mm/min; ISO 178
2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.84 GPa
412 ksi
ASTM D790
Izod Impact, Notched 0.430 J/cm
0.806 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.81 J/cm
7.14 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J

@Temperature 23.0 °C
5.90 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
42.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 109 µm/m-°C

@Temperature -30.0 - 30.0 °C
60.6 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
105 °C

@Thickness 3.20 mm
221 °F

@Thickness 0.126 in
unannealed; ASTM D648