SABIC Innovative Plastics LNP THERMOCOMP MC002 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MC002 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 3.7 % | 3.7 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 6.29 GPa | 912 ksi | 1 mm/min; ISO 527 |
| 11.17 GPa | 1620 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 4.70 GPa | 682 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.59 GPa | 1390 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Victrex® PEEK 150G903 Black Polyetheretherketone, Unreinforced
- Michelman® Michem® Guard 350 Nonionic, Fischer-Tropsch dispersion
- Momentive Performance Materials LVG342A Low Volatile Silicone Adhesive Component, White
- SABIC Innovative Plastics Ultem DH1004F PEI (Europe-Africa-Middle East)
- Star Plastics PC703 Molding Grade PC with release
- Sibur MPP 15-06V Frost Resistant Polypropylene
- SABIC Innovative Plastics NORYL 844 PPE+PS (Asia Pacific)
- Wanhua Chemical Wanthane® WHT-1495B Polyester Based TPU
- ATI Allvac® VascoMax® C-300 Specialty Steel, Heat Treatment: 927°C (1700°F) + Age
- LATI Latigea B02 H6 Bio-Polymer
Copyright © lookpolymers.com All Rights Reserved