SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGN2000 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Water Absorption | 0.16 % @Time 86400 sec |
0.16 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 91 | 91 | ASTM D785 |
| Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 86.0 MPa | 12500 psi | SABIC - Japan Method |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | SABIC - Japan Method |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 | |
| Flexural Strength | 127 MPa | 18400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 147 MPa | 21300 psi | ASTM D790 | |
| Flexural Modulus | 5.29 GPa | 767 ksi | ASTM D790 |
| 5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 29.0 - 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 - 29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| CTE, linear, Parallel to Flow | 4.10 µm/m-°C @Temperature -30.0 - 30.0 °C |
2.28 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 148 °C @Thickness 6.40 mm |
298 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C @Thickness 6.40 mm |
293 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
UL 94 |
| V-0 @Thickness 1.52 mm |
V-0 @Thickness 0.0598 in |
UL 94 | |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 50.0 - 60.0 Hz |
3.2 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 19.2 kV/mm @Thickness 3.20 mm |
488 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.00090 @Frequency 50.0 - 60.0 Hz |
0.00090 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Abatron 7505-2A/501B Filled Potting Compound (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 4650N (50401N) High Density Polyethylene
- Karina 32/82-FC-(CS) Orange Color Concentrate for PVC
- SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC
- SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66
- Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
- Sinotek Materials R20 C Carbon Rod for Dry Battery
- A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin
- Colorite Polymers CS6033UL Wire and Cable Insulation Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved