SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* Lexan_JK2000 compound is a 22% GR, ECO-compliant FR, PC+ABS for thinwall molding applications.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.00050 - 0.0015 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0015 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0015 - 0.0035 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0035 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 260 °C
22 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
36 g/10 min

@Load 1.20 kg,
Temperature 300 °C
36 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
5 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 5 mm/min; ASTM D638
59.0 MPa
8560 psi
5 mm/min; ISO 527
Elongation at Break 2.8 %
2.8 %
5 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 7.37 GPa
1070 ksi
5 mm/min; ASTM D638
7.66 GPa
1110 ksi
1 mm/min; ISO 527
Flexural Strength 103 MPa
14900 psi
1.3 mm/min, 50 mm span; ASTM D790
106 MPa
15400 psi
2 mm/min; ISO 178
Flexural Yield Strength 107 MPa
15500 psi
2 mm/min; ISO 178
Flexural Modulus 6.89 GPa
999 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.27 GPa
1050 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.31 J/cm
6.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J

@Temperature 23.0 °C
10.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
10.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 61.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
42.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C

@Thickness 3.20 mm
187 °F

@Thickness 0.126 in
unannealed; ASTM D648
89.0 °C

@Thickness 6.40 mm
192 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 93.0 °C
199 °F
Rate B/120; ISO 306
102 °C
216 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.990 mm
V-0

@Thickness 0.0390 in
UL 94