SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* LC006 is a compound based on Polyetheretherketone resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
1.413 g/cc
0.05105 lb/in³
ASTM D792
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
0.0800 %
0.0800 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 cm/cm

@Time 86400 sec
 0.0010 in/in

@Time 24.0 hour
 ASTM D955
0.0012 cm/cm

@Time 86400 sec
 0.0012 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0040 cm/cm

@Time 86400 sec
 0.0040 in/in

@Time 24.0 hour
 ASTM D955
0.0040 cm/cm

@Time 86400 sec
 0.0040 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 225 MPa
32600 psi
ASTM D638
230 MPa
33400 psi
ISO 527
Elongation at Break 1.5 %
1.5 %
ASTM D638
1.5 %
1.5 %
ISO 527
Tensile Modulus 24.7 GPa
3580 ksi
1 mm/min; ISO 527
30.75 GPa
4460 ksi
50 mm/min; ASTM D638
Flexural Strength 325 MPa
47100 psi
ASTM D790
346 MPa
50200 psi
ISO 178
Flexural Modulus 20.2 GPa
2930 ksi
ASTM D790
24.3 GPa
3520 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.08 J/cm
11.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 42.0 kJ/m²
20.0 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 12.0 J
8.85 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic 0.30
0.30
ASTM D3702 Modified
Coefficient of Friction, Static 0.32
0.32
ASTM D3702 Modified
K (wear) Factor 111 x 10-8 mm³/N-M
55.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.67 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
12.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.72 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 29.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
29.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) >= 240 °C
>= 464 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
>= 298 °C

@Thickness 3.20 mm
 >= 568 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) >= 240 °C
>= 464 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
>= 298 °C

@Thickness 3.20 mm
 >= 568 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.770 mm
 V-0

@Thickness 0.0303 in
 UL 94 by SABIC-IP