SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* JF002 is a compound based on Polyethersulfone resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 106 MPa
15400 psi
5 mm/min; ISO 527
Elongation at Break 4.2 %
4.2 %
5 mm/min; ISO 527
Tensile Modulus 4.50 GPa
653 ksi
1 mm/min; ISO 527
Flexural Strength 155 MPa
22500 psi
2 mm/min; ISO 178
Flexural Modulus 4.10 GPa
595 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 38.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 21.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Flammability, UL94 V-0

@Thickness 0.500 mm
 V-0

@Thickness 0.0197 in
 UL 94