SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP IC006 PA 6/12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* IC006 is a compound based on Nylon 6/12 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ASTM D792
1.21 g/cc
0.0437 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0025 cm/cm

@Time 86400 sec
 0.0025 in/in

@Time 24.0 hour
 ISO 294
0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
 0.010 - 0.012 in/in

@Time 24.0 hour
 ASTM D955
0.011 cm/cm

@Time 86400 sec
 0.011 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 200 MPa
29000 psi
ISO 527
201 MPa
29200 psi
ASTM D638
Tensile Strength, Yield 200 MPa
29000 psi
ISO 527
201 MPa
29200 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ISO 527
2.2 %
2.2 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ISO 527
2.2 %
2.2 %
ASTM D638
Tensile Modulus 17.92 GPa
2599 ksi
50 mm/min; ASTM D638
18.76 GPa
2721 ksi
1 mm/min; ISO 527
Flexural Strength 262 MPa
38000 psi
ASTM D790
284 MPa
41200 psi
ISO 178
Flexural Modulus 12.41 GPa
1800 ksi
ASTM D790
15.4 GPa
2230 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.90 J/cm
14.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 19.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
20.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 213 °C
415 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
212 °C

@Thickness 3.20 mm
 414 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
 387 °F

@Thickness 0.126 in
 unannealed; ASTM D648