SABIC Innovative Plastics LNP THERMOCOMP HF006EU PA11 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP HF006EU PA11 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* HF006EU is a compound based on PA 11 resin containing Glass Fiber. Added features include: Easy Molding, UV-Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Water Absorption | 0.18 % @Time 86400 sec |
0.18 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 117 MPa | 17000 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 169 MPa | 24500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.60 GPa | 812 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C @Temperature 23.0 - 60.0 °C |
83.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 173 °C | 343 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- 3M Dyneon™ 1641 PTFE Powder (discontinued **)
- Mi-Tech Metals HD18D Tungsten-Based Metal
- Multibase Multi-Flex® D 4201 TPE Thermoplastic Elastomer
- Loctite® Durabond® E-214HP Epoxy Adhesive
- ConocoPhillips 68 Ultra-Clean Super Hydraulic Oil
- 3M 6145 Kraft Light Duty Reinforced Water Activated Tape
- Ashley Polymers Ashlene® PC/ABS Alloy 304
- ConocoPhillips 32 Spectrum Cutting Oil
- Polimeri Europa KOBLEND PCA 638 PC+ABS (discontinued **)
- Victrex® PEEK 381G Medium Viscosity
Copyright © lookpolymers.com All Rights Reserved