SABIC Innovative Plastics LNP THERMOCOMP EX00781H PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EX00781H PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* EX00781H is a compoud based on Polyetherimide containng Proprietary Filler(s). Added feature of this material is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Melt Flow | 12.3 g/10 min @Load 6.60 kg, Temperature 337 °C |
12.3 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 340 °C |
10 g/10 min @Load 11.0 lb, Temperature 644 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | 5 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | Type I, 5 mm/min; ASTM D638 |
| 91.0 MPa | 13200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.5 % | 5.5 % | 5 mm/min; ISO 527 |
| 5.9 % | 5.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.25 GPa | 471 ksi | 1 mm/min; ISO 527 |
| 3.32 GPa | 482 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 148 MPa | 21500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.15 GPa | 457 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.31 GPa | 480 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 189 °C @Thickness 3.20 mm |
372 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 213 °C | 415 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Omnia Plastica PEI Polyetherimide
- SABIC Innovative Plastics LNP FARADEX AS002 ABS
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 52A
- Gromax BFG20-FN00N1 Nylon 6 20% Glass Filled (Dry)
- Sharadaa Ceramics Z Block
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- Zeon Chemicals Nipol® DN171 Polyblend Nitrile Elastomer
- A. Schulman ComAlloy Hiloy® 625 Nylon 6/6, Glass Reinforced
- Phillips 66 COPYLENE® CH200LN-02 Polypropylene, Homopolymer, Rx grade, Nucleated, Lube, Injection Molding
- SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved